Optical glass and optical element

ABSTRACT

The invention provides a high-refraction low-dispersion optical glass with refractive index of 1.76-1.80 and Abbe number of 47-51. The optical glass, comprising the following components by weight percentage: 0-3% of SiO2; 25-40% of B2O3; 20-40% of La2O3; 12-25% of Gd2O3; 6.5-15% of ZrO2; greater than 10% but less than or equal to 20% of ZnO; 0-5% of Ta2O5; 0-5% of Nb2O5; 0-10% of Li2O; less than 0.45 of (Ta2O5+Nb2O5)/(ZnO+Li2O); 0-10% of Y2O3; and below 625° C. of glass transition temperature Tg. With reasonable component ratio, the high-refraction low-dispersion optical glass favorable to precision is molding with excellent transmittance can be easily enabled while realizing the required optical constant of the glass of the present invention.

TECHNICAL FIELD

The invention relates to an optical glass with high-refraction low-dispersion, and a glass preform and an optical element made of the above optical glass.

BACKGROUND

For optical glass, refractive index, Abbe number and transmittance are its core optic characters. The refractive index and Abbe number decide the basic functions of glass, and the optical glass with the refractive index of 1.76-1.80 and Abbe number of 47-51 is a high-refraction low-dispersion optical glass. The application of such high performance glass in an optical system can shorten the length of lens and improve the imaging quality.

In order to meet the requirements of precision molding of optical glass, the transition temperature Tg of optical glass is required. Under the premise of realizing the same optical performance, how to realize low Tg temperature of glass and guarantee excellent transmittance is the objective of research and development at present. CN102050571A discloses a high refractive index optical glass with a refractive index of 1.77-1.83 and Abbe number of 44-51, but its Tg temperature is higher, so it is not suitable for low-cost precision molding. In addition, the glass contains a lot of Ta₂O₅, while Ta₂O₅ belongs to an expensive metal oxide, and intensive use may increase the material cost of the high-refraction low-dispersion optical glass and reduce the product economy. Additionally, it further contains SnO₂, which is not only difficult to melt, easy to form impurities in glass, and affect the inherent quality and processing performance of glass, but also can improve the pigmentation degree of glass, reduce the transmittance. The optical element of the optical system for camera shooting or projecting has higher requirements for the transmittance of optical glass, and the transmission light of the optical system will be affected if the transmission light of the lens formed by high-refraction low-dispersion optical glass is not enough, thus influencing the imaging quality.

SUMMARY

The technical problem to be solved by the present invention is to provide a high-refraction low-dispersion optical glass with refractive index of 1.76-1.80 and Abbe number of 47-51. The glass has an excellent transmittance when the content of Ta₂O₅ in glass component is reduced.

The present invention also provides a glass preform and an optical element made of the above optical glass.

The technical scheme to solve the technical problem in the present invention is: an optical glass, comprising the following components by weight percentage: 0-3% of SiO₂; 25-40% of B₂O₃; 20-40% of La₂O₃; 12-25% of Gd₂O₃; 6.5-15% of ZrO₂; greater than 10% but less than or equal to 20% of ZnO; 0-5% of Ta₂O₅; 0-5% of Nb₂O₅; 0-10% of Li₂O; less than 0.45 of (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O); 0-10% of Y₂O₃; and below 625° C. of glass transition temperature Tg.

Further, it comprises 0-10% of GeO₂; 0-10% of Bi₂O₃; 0-10% of Al₂O₃; 0-10% of Na₂O; 0-10% of K₂O; 0-1% of CeO₂; 0-1% of Sb₂O₃; 0-10% of RO, in which RO is one or more of MgO, CaO, SrO or BaO.

Further, it comprises 0-5% of Al₂O₃ and/or 0-5% of Na₂O and/or 0-5% of K₂O and/or 0-5% of GeO₂ and/or 0-5% of Bi₂O₃ and/or 0-0.5% of CeO₂ and/or 0-0.5% of Sb₂O₃ and/or 0-5% of RO.

Further, it comprises 0-1% of Al₂O₃ and/or 0-1% of Na₂O and/or 0-1% of K₂O and/or 0-1% of GeO₂ and/or 0-1% of Bi₂O₃ and/or 0-1% of RO.

Further, (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is 0.30-1.50; La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.38-0.75; ZnO/(B₂O₃+SiO₂) is 0.25-0.65.

Further, it comprises 28.5-35% of B₂O₃ and/or 25-35% of La₂O₃ and/or 14-22% of Gd₂O₃ and/or 6.5-10% of ZrO₂ and/or 11-16% of ZnO and/or 0-1% of SiO₂ and/or 0-1% of Ta₂O₅ and/or 0-1% of Nb₂O₅ and/or 0-7% of Y₂O₃ and/or 0-5% of Li₂O.

Further, it comprises 29-32% of B₂O₃ and/or 27-32% of La₂O₃ and/or 15-20% of Gd₂O₃ and/or 6.5-8.5% of ZrO₂ and/or 11-14.5% of ZnO and/or 0-0.5% of SiO₂ and/or 0-0.5% of Ta₂O₅ and/or 0-0.5% of Nb₂O₅ and/or 0.1-5% of Y₂O₃ and/or 0-1% of Li₂O.

Further, (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) is less than 0.10, and/or La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.45-0.70, and/or ZnO/(B₂O₃+SiO₂) is 0.30-0.55, and/or (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is 0.48-1.10.

Further, (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) is less than 0.07, and/or La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.55-0.65, and/or ZnO/(B₂O₃+SiO₂) is 0.30-0.50, and/or (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is 0.50-1.0.

Further, of glass the refractive index is 1.76-1.80, the Abbe number is 47-51 and the density is below 5.00 g/cm³.

A glass preform is made of the above optical glass.

An optical element is made of the above optical glass.

The beneficial effects of the present invention are that the transmittance of glass becomes excellent without introducing SnO₂, the product cost is optimized by reducing the content of Ta₂O₅, and that with reasonable component ratio, the high-refraction low-dispersion optical glass in favor of precision molding and with excellent transmittance, as well as the glass preform and optical element made of the optical glass can be easily enabled while realizing the required optical constant of the glass.

DETAILED DESCRIPTION

I . Optical Glass

The composition of the optical glass in the present invention will be described in detail below, the content and total content of each glass component is expressed by wt % unless otherwise specified, and the ratio of content to total content of glass component is expressed by weight ratio. In addition, in the following description, if referred to below or above the prescribed value, the prescribed value is included.

B₂O₃ is a glass network forming component having effects of improving glass meltability and reducing glass transition temperature. In order to achieve the above-mentioned effect, 25% or more B₂O₃ is introduced in the present invention. However, when the introduced amount exceeds 40%, the glass stability will be lowered, so will the refractive index, such that the high refractive index of the present invention cannot be obtained. Therefore, the content of B₂O₃ in the present invention is 25-40%, preferably 28.5-35%, and more preferably 29-32%.

SiO₂ is also a glass forming body, which is different from the loose chain layered network formed by B₂O₃. SiO₂ forms silica-oxygen tetrahedron three-dimensional network in the glass, being very dense and solid. This network is added into the glass to reinforce the loose boron oxide triangular body [BO₃] network to make it dense, thereby enhancing the high temperature viscosity of the glass. At the same time, the addition of the silica-oxygen tetrahedron three-dimensional network and the improved capability of glass network isolating devitrification cations and anions such as La₂O₃, Nb₂O₅ increase the devitrification threshold, so that the anti-devitrification property of the glass is improved. However, if the content of SiO₂ is increased without limitation, difficulties in dissolution will arise. On the other hand, the content of rare earth oxides including La₂O₃ and Gd₂O₃ will be increased inevitably to main high refractive index and low dispersion, while the solubility of SiO₂ to La₂O₃ is relatively low, thus resulting in sharp drop of devitrification resistance of glass. Therefore, the content of SiO₂ in the present invention is confined to 0-3%, preferably 0-1%, and further preferably 0-0.5%.

La₂O₃ is an essential component for obtaining the optical properties required for the present invention. When the content of La₂O₃ is less than 20%, it is difficult to achieve the required optical properties; but when the content exceeds 40%, the devitrification resistance and melting property of glass will deteriorate. Therefore, the range of the content of La₂O₃ in the present invention is 20-40%, preferably 25-35%, and more preferably 27-32%.

Gd₂O₃ is an effective component to obtain an optical glass of high refractive index. The stability of glass can be improved through the coexistence of Gd₂O₃ and La₂O₃ in the present invention, but the above effect will not be obvious when the content of Gd₂O₃ is lower than 12%; when such content exceeds 25%, the devitrification resistance of glass will reduce, and the stability of the glass formed will then be worsened. Therefore, the range of the content of Gd₂O₃ in the present invention is 12-25%, preferably 14-22%, and more preferably 15-20%.

Y₂O₃ is also preferably introduced into the high-refraction low-dispersion components of the present invention, which can improve the meltability and devitrification resistance of glass and reduce the upper limit of devitrification temperature of glass. However, if its content exceeds 10%, the stability and devitrification resistance of glass will decrease. Therefore, the range of the content of Y₂O₃ is 0-10%, preferably 0-7%, and more preferably 0.1-5%.

In La₂O₃, Gd₂O₃ and Y₂O₃, the component with the greatest impact on improving glass refractive index and maintaining glass stability is La₂O₃. However, if only La₂O₃ is used in the optical glass of the present invention, it is difficult to ensure the sufficient glass stability. Thus, the introduced amount of La₂O₃ in the present invention is relatively great, and La₂O₃ is made coexist with Gd₂O₃; or preferably La₂O₃ and Gd₂O₃ are made coexist with Y₂O₃; the more preferable range of La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.38-0.75, further preferable 0.45-0.70, and furthermore preferable 0.55-0.65, then, the high-refraction low-dispersion glass with excellent stability can be obtained, while the glass is not easy to be colored.

Nb₂O₅ has an effect of improving glass refractive index and lowering liquidus temperature, as well as improving the devitrification resistance and chemical durability of glass. If its content exceeds 5%, the dispersion of glass will be improved, and the optical property of the glass in the present invention cannot be obtained. Therefore, the range of the content of Nb₂O₅ is 0-5%, preferably 0-1%, more preferably 0-0.5%.

Ta₂O₅ can increase the refractive index and does better than Nb₂O₅ in maintaining the low dispersion of glass. However, Ta₂O₅ is very expensive when compared with other components, hence, its usage is reduced in the present invention from the perspectives of utility and cost. The range of the content of Ta₂O₅ in the present invention is 0-5%, preferably 0-1%, more preferably 0-0.5%, and further preferably not introduced.

The appropriate addition of ZnO in glass can improve the chemical stability and reduce the high-temperature viscosity and temperature Tg of glass. However, if excessive ZnO is added, the devitrification resistance of glass will decline, and the relatively low high-temperature viscosity brings challenges to molding. In this glass system, the temperature Tg cannot meet the design requirements, if the content of ZnO is less than 10%. If the content is higher than 20%, the devitrification resistance of glass will decrease and the high-temperature viscosity cannot meet the design requirements. Therefore, the content of ZnO is confined to be greater than 10% but less than or equal to 20%, preferably 10.2-20%, more preferably 11-16%, further preferably 11-14.5%.

In order to obtain an easy-melting glass with a relatively low temperature Tg and good stability, the inventor, through a large number of experimental studies, has found that the stability and temperature Tg of glass can reach the best balance to obtain a product of better quality when the range of ZnO/(B₂O₃+SiO₂) is 0.25-0.65, preferably 0.30-0.55 and further preferably 0.30-0.50.

ZrO₂ is a high-refraction oxide, which can significantly improve the refractive index and chemical stability of glass. In the present invention, ZrO₂ also plays a role in improving the abnormal dispersion of glass which is favorable to eliminate secondary spectrum in optical design. The aforesaid effect will not be significant if its content is excessively low, while the risks of glass devitrification will be remarkably increased if the content is excessive. Therefore, the content is confined to 6.5-15%, preferably 6.5-10%, and more preferably 6.5-8.5%.

The optical transmittance is a quite important performance index of optical glass. When the range of (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is controlled at 0.30-1.50, preferably at 0.48-1.10, more preferably at 0.50-1.00, and furthermore preferably at 0.50-0.70, the coloring of glass can be suppressed, and the heat stability and devitrification resistance of glass can be improved, while enabling preferable ranges of refractive index and Abbe number of the present invention.

The introduction of a small amount of Al₂O₃ can improve the stability and chemical stability of glass. However, when the content exceeds 10%, a tendency of meltability deterioration and devitrification resistance reduction of glass is shown. Therefore, the content of Al₂O₃ in the present invention is 0-10%, preferably 0-5%, more preferably 0-1%, and further preferably not introduced.

The addition of Li₂O into glass component can effectively lower the temperature Tg. But the optical glass with low softening point is usually smelted with platinum or platinum alloy vessels. During high temperature smelting, Li⁺ in the glass component easily corrodes platinum or platinum alloy vessels, resulting in more platinum-containing foreign matters in the finished glass, leading to a decline in the quality of the glass. On the other hand, when such glass is used for precision molding, the glass element is easy to have a fuzzy surface, because the die is generally coated with carbon-bearing releasing agent, Li in the glass component is easy to have a reaction with carbon in the releasing agent, thereby generating a rough opaque film on the surface of the glass element. Therefore, the content is confined to 0-10%, preferably 0-5%, and more preferably 0-1%.

Na₂O and K₂O are optional components effective in lowering Tg, and if the content thereof is excessive, it is easy to cause increased devitrification temperature and vitrification difficulties, so that the content are confined to 0-10%, more preferably 0-5%, and further preferably 0-1%.

Based on a large number of experimental studies, the inventor has found that the ratio of the total content of Ta₂O₅+Nb₂O₅ to the total content of ZnO+Li₂O has a greater impact on the chemical stability and temperature Tg of the glass. When (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) exceeds 0.45, Tg will increase significantly, unfavorable to precision molding; when (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) is less than 0.10, the chemical stability of the glass will be greatly enhanced and the glass density will be effectively decreased. In this regard, for the glass of the present invention, (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) is confined to be less than 0.45, preferably less than 0.10, more preferably less than 0.07, and further preferably less than 0.01.

RO (one or more of MgO, CaO, SrO or BaO) can improve the meltability and adjust the optical property of glass. However, when the content of RO exceeds 10%, the devitrification resistance of glass will be reduced. Therefore, the content of RO in the present invention is 0-10%, more preferably 0-5%, and further preferably 0-1%.

Bi₂O₃ can increase the refractive index of glass, but its excessive content will lower the transmittance on the long side of short waves in the visible region and show a tendency of coloring. Therefore, the content of Bi₂O₃ provided by the present invention is preferably 0-10%, more preferably 0-5%, further preferably 0-1%, and furthermore preferably not introduced.

GeO₂ can effectively improve the stability and devitrification resistance of glass as well. As GeO₂ is very expensive, the preferable content of GeO₂ then is 0-10%, more preferably 0-5%, further preferably 0-1%, and furthermore preferably not introduced.

The clarification effect of glass can be increased by adding a small amount of Sb₂O₃ and CeO₂. However, when the content of Sb₂O₃ exceeds 1%, the glass will be faced with the risks of lowered devitrification resistance and increased dispersion, and its strong oxidation will promote the deterioration of molding die. Therefore, the preferable addition of Sb₂O₃ is 0-1%, more preferably 0-0.5%, and further preferably not added. The role and the proportion of addition of CeO₂ are consistent with Sb₂O, so its preferable content is 0-1%, more preferably 0-0.5%, and further preferably not added.

F is an ingredient having great effects of improving light refraction and lowering temperature coefficient of a relative refractive index. However, it is served as the optical element difficultly on account that an environmental load problem is caused by volatilization in its production process and a heterogeneous part is formed for its volatilization from a glass surface in a forming temperature area. Furthermore, the ingredient F is not introduced to realize excellent quality of the glass and good optical constant consistency in the present invention.

Hereinafter, the properties of the optical glass provided by the present invention will be described.

[Optical Constant of Optical Glass]The optical glass provided by the present invention is a high-refraction low-dispersion glass. A lens made of the high-refraction low-dispersion glass is mostly combined with a lens made of high-refraction high-dispersion glass for chromatic aberration correction. The optical glass provided by the present invention has a glass refractive index nd in the range of 1.76-1.80, preferably in the range of 1.76-1.79, more preferably in the range of 1.76-1.78, and further preferably in the range of 1.77-1.78, from the viewpoint of imparting optical properties suitable for its use. The range of the Abbe number v_(d) of the glass provided by the present invention is in the range of 47-51, preferably in the range of 48-50 and more preferably in the range of 49-50.

[Coloring of Optical Glass]

The short-wave transmission spectrum characteristics of the glass provided by the present invention are represented by pigmentation zo degree (λ₈₀/λ₅). λ₈₀ refers to a wavelength corresponding to a glass transmittance of 80%, and λ₅ is a wavelength corresponding to a glass transmittance of 5%. The measurement of λ₈₀ is carried out using a glass having a thickness of 10±0.1 mm

with two opposing planes parallel to each other and optically polished to measure the spectral transmittance in the wavelength region from 280 nm to 700nm and a wavelength exhibiting 80% of the transmittance. The spectral transmittance or transmittance is an amount indicated by I_(out)/I_(in) in the case where the light of an intensity I_(in) is incident perpendicularly to the above surface of the glass, passes through the glass and emits the light of an intensity I_(out) from a plane, and includes the transmittance of the surface reflection lost on the above surface of the glass. The higher the refractive index of the glass, the greater the surface reflection loss. Thus, a small value of λ₈₀ means that the glass is colored very little in the high refractive index glass.

For the optical glass of the present invention, λ₈₀ is less than or equal to 400 nm, preferably less than or equal to 395 nm, more preferably less than or equal to 390 nm, further preferably less than or equal to 385 nm, and furthermore preferably less than or equal to 380 nm. λ₅ is less than or equal to 300 nm, preferably less than or equal to 290 nm, more preferably less than or equal to 285 nm, further preferably less than or equal to 280 nm.

[Density of Optical Glass]

The density of optical glass is the mass per unit volume at a temperature of 20° C., expressed in g/cm³.

The density of the glass provided by the present invention is below 5.00 g/cm³, preferably below 4.80 g/cm³, more preferably below 4.70 g/cm³, and further preferably below 4.60 g/cm³.

[Transition Temperature of Optical Glass]

The optical glass will gradually turn from a solid state to a plastic state within a certain temperature range. The transition temperature refers to the temperature at which the glass sample is heated from room temperature to sag temperature, corresponding to an intersection between extending lines of linear parts of a low temperature region and a high temperature region.

The transition temperature Tg of the glass provided by the present invention is below 625° C., preferably below 620° C., more preferably below 615° C., and further preferably below 610° C.

II. Optical Preform and Optical Element

Hereinafter, the optical preform and the optical element of the present invention will be described.

The optical preform and the optical element provided by the present invention are both made of the optical glass provided by the present invention described above. The optical preform provided by the present invention has a high refractive index and a low dispersion. The optical element provided by the present invention has a high refractive index and a low dispersion, which can provide such optical elements as various lenses and prisms having a high optical value at a low cost.

Examples of the lens include various lenses with spherical or aspheric surfaces, such as concave meniscus lens, convex meniscus lens, biconvex lens, biconcave lens, planoconvex lens and planoconcave lens.

This lens and a lens made of high-refraction high-dispersion glass are combined to correct the chromatic aberration, suitable as a lens for chromatic aberration correction. In addition, the lens is also effective for the compactness of the optical system.

In addition, for prism, due to the high refractive index, by combining into the optical system and by directing to the desired direction via curved optical path, a compact wide-angle optical system can be realized.

[Optical Glass Embodiment]

The present invention is illustrated by the following embodiments, but shall not be limited to them.

The method of melting and molding optical glass can be carried out by using the technology known to those skilled in the art. Weigh and evenly mix the glass raw materials (carbonate, nitrate, sulfate, hydroxide, oxide, boric acid, etc.) in the proportions of glass oxides, then put into a smelting device (such as platinum crucible), cool to below 1250° C. after appropriate mixing, clarification and homogenization at 1150-1400° C., pour or leak in a molding die, and finally conduct post-processing including annealing, processing, etc., or complete compression molding directly with precision profiling technology.

In addition, the characteristics of glass are measured by following methods, and the results are shown in Tables 1-9.

(1) Refractive Index nd and Abbe Number vd

The refractive index and Abbe number are tested as per the method specified in GB/T7962.1-2010.

(2) Pigmentation Degree of Glass (λ₈₀, λ₅)

The spectral transmittance is measured by using a glass sample having a thickness of 10±0.1 mm with two opposing planes optically polished, and calculated on the basis of the result.

(3) Transition Temperature of Glass (Tg)

Measurement is made as per the method specified in GB/T7962.16-2010.

(4) Proportion (p)

Measurement is made as per the method specified in GB/T7962.20-2010.

TABLE 1 Embodiment Composition 1 2 3 4 5 6 7 8 9 10 SiO₂ 0.14 2.84 0.82 0.20 0.67 0.51 0.75 0.36 0.48 0.87 B₂O₃ 39.57 28.51 29.04 28.9 34.22 31.08 34.16 29.15 35.68 29.03 La₂O₃ 20.33 21.73 34.36 25.12 22.14 28.12 25.03 38.85 28.16 26.14 Gd₂O₃ 14.62 12.07 13.44 21.4 15.39 16.3 18.82 13.08 15.24 12.63 Y₂O₃ 0.17 9.85 0.53 0 1.35 2.44 0 0.51 0 6.52 Ta₂O₅ 0.08 4.55 0 0 0.06 0 0.36 0 0.11 0.84 Nb₂O₅ 4.32 0.16 0.27 0.63 0.87 0.37 0.47 0 0.34 0.26 ZrO₂ 6.52 6.72 9.71 7.11 8.36 7.24 8.33 6.74 7.64 7.66 ZnO 10.25 11.32 11.37 15.64 14.60 13.22 12.08 11.17 12.35 14.36 Bi₂O₃ 0 0.20 0 0 0 0 0 0 0 0 GeO₂ 0 0 0 0 1.10 0 0 0 0 0 Al₂O₃ 0 0.14 0 0 0 0 0 0 0 0 Li₂O 0.16 0.54 0.14 0.65 0.64 0.72 0 0.14 0 1.64 Na₂O 0 0 0.32 0 0.21 0 0 0 0 0 K₂O 0 0 0 0 0.20 0 0 0 0 0 Sb₂O₃ 0.06 0 0 0 0.07 0 0 0 0 0.05 CeO₂ 0 0.03 0 0 0 0 0 0 0 0 RO 3.78 1.34 0 0.35 0.12 0 0 0 0 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.5789 0.4978 0.7109 0.5400 0.5694 0.6001 0.7408 0.5708 0.6488 0.5772 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0.4227 0.3971 0.0235 0.0387 0.0569 0.0265 0.0687 0 0.0364 0.0688 (ZnO + Li₂O) ZnO/(B₂O₃ + SiO₂) 0.2581 0.3611 0.3808 0.5375 0.4185 0.4185 0.3460 0.3785 0.3415 0.4803 (ZrO₂ + Y₂O₃)/(Nb₂O₅ + 0.3532 1.3549 0.7469 0.3227 0.5972 0.5807 0.4318 0.5543 0.4904 1.1001 Gd₂O₃) nd 1.76354 1.77180 1.78343 1.78065 1.77631 1.77416 1.77221 1.78326 1.77545 1.77915 vd 50.86 48.25 48.93 49.31 49.52 49.51 48.36 49.35 49.28 49.66 ρ (g/cm³) 4.625 4.506 4.515 4.527 4.508 4.502 4.615 4.582 4.517 4.462 λ80/λ5 385/286 384/285 381/282 384/285 381/280 380/280 379/280 381/284 384/282 383/281 Tg (° C.) 623.5 620.4 618.3 609.2 614.4 614.2 617.2 615.3 614.0 613.2

TABLE 2 Embodiment Composition 11 12 13 14 15 16 17 18 19 20 SiO₂ 0.37 0.66 0.52 0.85 1.26 1.67 2.14 1.06 0.85 0.63 B₂O₃ 36.23 29.16 30.12 33.53 31.54 32.74 29.32 37.45 32.54 37.22 La₂O₃ 22.36 34.65 24.89 23.62 29.56 21.00 26.47 21.88 24.73 23.98 Gd₂O₃ 13.52 13.94 21.63 14.25 12.74 20.14 15.03 19.66 20.14 14.47 Y₂O₃ 1.33 0 0 6.35 0 0 2.45 0 0 3.32 Ta₂O₅ 0.47 0 0.31 0 0 0.08 0 0 0 0 Nb₂O₅ 0.62 0 0.62 0.52 0 0 0.21 0 0.14 0 ZrO₂ 7.26 9.24 6.95 7.33 7.26 7.05 8.11 6.92 6.88 7.58 ZnO 16.00 12.35 14.36 13.2 16.9 12.47 15.24 12.7 14.32 11.58 Bi₂O₃ 1.30 0 0 0 0 0 0 0.33 0 0 GeO₂ 0.11 0 0 0 0 0 0 0 0 1.00 Al₂O₃ 0 0 0 0 0 4.85 0 0 0 0 Li₂O 0.36 0 0.27 0.35 0.74 0 0.26 0 0.26 0.22 Na₂O 0 0 0 0 0 0 0 0 0.14 0 K₂O 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0.07 0 0 0 0 0 0.03 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 RO 0 0 0.33 0 0 0 0.74 0 0 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.6009 0.7131 0.5350 0.5341 0.6988 0.5105 0.6023 0.5267 0.5511 0.5741 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/(ZnO + 0.0613 0 0.0636 0.0384 0 0.0064 0.0135 0 0.0096 0 Li₂O) ZnO/(B₂O₃ + SiO₂) 0.4372 0.4142 0.4687 0.3839 0.5152 0.3624 0.4844 0.3298 0.4289 0.3059 (ZrO₂ + Y₂O₃)/ 0.6075 0.6628 0.3124 0.9262 0.5699 0.3500 0.6929 0.3520 0.3393 0.7533 (Nb₂O₅ + Gd₂O₃) nd 1.77034 1.77415 1.77326 1.77185 1.78036 1.77624 1.77241 1.76854 1.77226 1.77471 vd 49.35 49.52 49.28 48.92 48.64 49.57 49.63 49.55 49.78 49.58 ρ (g/cm³) 4.526 4.582 4.563 4.522 4.515 4.637 4.567 4.528 4.495 4.521 λ80/λ5 3381/281 3385/282 3382/284 3383/282 3381/283 3380/281 3382/280 3385/286 3386/281 387/285 Tg (° C.) 610.3 615.7 616.2 614.3 614.0 617.5 616.2 614.5 614.7 3620.1

TABLE 3 Embodiment Composition 21 22 23 24 25 26 27 28 29 30 SiO₂ 0.49 1.17 0.68 0.56 0.27 0.83 1.32 0.79 1.62 0.86 B₂O₃ 29.33 32.08 30.17 31.5 33.14 30.24 25.61 31.45 28.97 33.14 La₂O₃ 28.17 25.97 27.44 33.37 30.25 28.33 29.65 26.33 30.32 31.38 Gd₂O₃ 18.24 20.16 20.76 13.32 15.27 17.86 23.44 19.16 16.32 15.32 Y₂O₃ 1.72 0 2.13 0 0.85 1.22 0 0 0 0 Ta₂O₅ 0 0 0 0 0.06 0 0 0 0 0 Nb₂O₅ 0 0.04 0 0 0 0 0 0 0.25 0 ZrO₂ 7.33 6.95 7.45 6.92 7.08 6.87 7.15 7.64 7.36 6.75 ZnO 12.28 13.41 11.37 14.33 12.66 13.1 12.44 13.72 11.95 12.55 Bi₂O₃ 0 0 0 0 0 0 0.39 0 0 0 GeO₂ 0 0 0 0 0 0 0 0 0 0 Al₂O₃ 0.33 0 0 0 0 0 0 0 0 0 Li₂O 0.35 0 0 0 0.42 0.52 0 0.06 0.41 0 Na₂O 0 0.22 0 0 0 0 0 0.85 0.32 0 K₂O 0 0 0 0 0 0.27 0 0 0 0 Sb₂O₃ 0.24 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0.05 0 0 0.18 0 RO 1.52 0 0 0 0 0.71 0 0 2.30 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.5853 0.5630 0.5452 0.7147 0.6524 0.5976 0.5585 0.5788 0.6501 0.6719 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0 0.0030 0 0 0.0046 0 0 0 0.0202 0 (ZnO + Li₂O) ZnO/ 0.4118 0.4033 0.3686 0.4470 0.3789 0.4216 0.4619 0.4256 0.3907 0.3691 (B₂O₃ + SiO₂) (ZrO₂ + Y₂O₃)/ 0.4962 0.3441 0.4615 0.5195 0.5193 0.4530 0.3050 0.3987 0.4442 0.4406 (Nb₂O₅ + Gd₂O₃) nd 1.77542 1.77461 1.77682 1.77824 1.78025 1.77492 1.76954 1.77724 1.77452 1.77320 vd 48.95 49.22 49.62 49.37 49.52 49.55 49.75 49.19 48.95 49.37 ρ (g/cm³) 4.512 4.516 4.522 4.571 4.615 4.536 4.521 4.492 4.516 4.527 λ80/λ5 383/285 380/281 384/285 386/283 384/281 378/280 379/280 380/279 381/282 384/282 Tg (° C.) 615.2 617.3 616.2 614.3 614.5 615.1 614.7 613.8 617.4 614.3

TABLE 4 Embodiment Composition 31 32 33 34 35 36 37 38 39 40 SiO₂ 0.74 0.68 1.06 0.92 2.15 0.81 1.22 0.69 0.88 1.17 B₂O₃ 29.36 30.25 29.34 32.95 36.37 31.25 32.24 29.37 31.09 31.02 La₂O₃ 34.33 30.17 23.37 22.47 25.11 31.35 29.31 31.25 27.76 31.27 Gd₂O₃ 15.72 18.25 20.66 13.74 16.94 18.55 17.25 16.17 19.33 16.38 Y₂O₃ 0.93 0 5.29 7.82 0.65 0 0 1.54 0 0 Ta₂O₅ 0 0 0.31 0 0 0 0 0.14 0 0 Nb₂O₅ 0 0 0 0.35 0 0 0 0.32 0 0 ZrO₂ 6.62 8.03 7.15 7.22 6.58 7.19 7.05 6.85 6.75 7.50 ZnO 12.16 12.25 11.32 13.52 12.2 10.55 12.3 13.2 13.56 11.95 Bi₂O₃ 0 0.37 0 0 0 0 0 0 0 0 GeO₂ 0 0 0 0 0 0 0 0 0.63 0 Al₂O₃ 0 0 0.13 0 0 0 0 0.07 0 0 Li₂O 0.12 0 0.07 0.57 0 0.3 0.41 0.4 0 0 Na₂O 0.02 0 0 0 0 0 0.22 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0.08 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 RO 0 0 1.22 0.44 0 0 0 0 0 0.71 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.6734 0.6231 0.4738 0.5103 0.5881 0.6283 0.6295 0.6383 0.5895 0.6562 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0 0 0.0272 0.0248 0 0 0 0.0338 0 0 (ZnO + Li₂O) ZnO/ 0.4040 0.3961 0.3724 0.3992 0.3167 0.3291 0.3676 0.4391 0.4241 0.3712 (B₂O₃+ SiO₂) (ZrO₂ + Y₂O₃)/ 0.4803 0.4400 0.6021 1.0674 0.4268 0.3876 0.4087 0.5088 0.3492 0.4579 (Nb₂O₅ + Gd₂O₃) nd 1.77924 1.77514 1.77453 1.77402 1.77456 1.77425 1.77521 1.77762 1.77451 1.77406 vd 49.68 49.55 49.57 49.68 49.38 49.47 49.52 49.47 49.62 49.60 ρ (g/cm³) 4.517 4.522 4.503 4.516 4.572 4.550 4.517 4.536 4.498 4.510 λ80/λ5 382/281 381/281 384/282 381/283 380/281 383/281 386/284 381/280 386/285 381/281 Tg (° C.) 614.0 615.2 615.3 614.2 614.1 615.2 614.2 616.0 614.7 614.5

TABLE 5 Embodiment Composition 41 42 43 44 45 46 47 48 49 50 SiO₂ 0.29 0.64 0.72 1.05 0.82 0.93 0.38 1.85 1.08 0.52 B₂O₃ 32.15 31.52 32.7 30.16 32.50 29.47 31.29 30.66 33.51 30.74 La₂O₃ 28.33 30.48 28.10 26.33 29.07 31.26 29.32 27.91 24.06 31.03 Gd₂O₃ 19.48 17.22 16.30 18.25 16.70 18.16 18.22 13.29 20.36 15.96 Y₂O₃ 0 0 0 0 1.2 0 0.94 4.08 0.49 2.13 Ta₂O₅ 0 0 0 0 0.3 0 0 0 0.26 0 Nb₂O₅ 0 0.06 0 0.24 0.16 0 0 0.21 0 0 ZrO₂ 7.23 6.93 6.78 7.11 7.26 6.93 6.96 7.39 6.62 7.20 ZnO 12.34 11.88 13.65 12.25 11.85 13.05 12.55 14.03 13.39 12.42 Bi₂O₃ 0 0 1.23 0 0 0 0 0 0 0 GeO₂ 0 0 0 0 0 0 0.34 0 0 0 Al₂O₃ 0 0 0.07 0 0 0 0 0 0 0 Li₂O 0.18 0 0.45 0.65 0.14 0 0 0.58 0.23 0 Na₂O 0 0 0 0.17 0 0.20 0 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0.02 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 RO 0 1.25 0 3.79 0 0 0 0 0 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.5926 0.6390 0.6329 0.5906 0.6189 0.6325 0.6048 0.6164 0.5357 0.6317 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/(ZnO + 0 0.0051 0 0.0186 0.0384 0 0 0.0144 0.0191 0 Li₂O) ZnO/(B₂O₃ + SiO₂) 0.3804 0.3694 0.4084 0.3925 0.3556 0.4293 0.3963 0.4316 0.3871 0.3973 (ZrO₂ + Y₂O₃)/ 0.3711 0.4010 0.4160 0.3845 0.5018 0.3816 0.4336 0.8496 0.3492 0.5846 (Nb₂O₅ + Gd₂O₃) nd 1.77451 1.77462 1.77405 1.77415 1.77416 1.77408 1.77455 1.77426 1.77503 1.77502 vd 49.67 49.58 49.35 49.55 48.75 49.68 49.15 48.96 49.33 49.57 ρ (g/cm³) 4.512 4.520 4.497 4.596 4.513 4.527 4.510 4.506 4.502 4.511 λ80/λ5 381/284 380/280 382/280 381/283 380/279 381/282 381/281 380/282 385/284 380/279 Tg (° C.) 608.4 612.3 614.2 615.0 612.3 614.5 613.2 611.7 615.2 617.0

TABLE 6 Embodiment Composition 51 52 53 54 55 56 57 58 59 60 SiO₂ 1.03 1.21 0.92 1.74 0.66 1.18 1.25 1.83 0.62 1.05 B₂O₃ 33.25 37.55 31.22 29.61 30.72 30.98 34.09 30.59 31.47 26.58 La₂O₃ 28.64 21.64 27.66 29.04 31.33 29.47 22.33 29.34 30.19 31.5 Gd₂O₃ 15.47 17.14 18.30 19.24 15.92 17.33 17.99 18.36 16.19 17.58 Y₂O₃ 2.36 3.35 0 0 0 1.38 0 0.17 0 0 Ta₂O₅ 0 0 0 0.36 0 0 0 0 0 0.67 Nb₂O₅ 0 0.06 0 0 0 0 0 0 0 0.18 ZrO₂ 6.82 6.94 7.45 6.95 6.68 7.06 8.66 7.11 6.99 7.36 ZnO 12.06 11.85 12.75 13.06 13.36 12.15 15.2 12.49 13.65 12.62 Bi₂O₃ 0 0 0 0 0 0 0 0 0.89 0 GeO₂ 0 0 0 0 0 0.45 0 0 0 0 Al₂O₃ 0 0 0 0 0 0 0 0 0 0 Li₂O 0.37 0.23 0.84 0 0.66 0 0.48 0.11 0 0.71 Na₂O 0 0 0.32 0 0 0 0 0 0 0.32 K₂O 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0.07 CeO₂ 0 0.03 0 0 0 0 0 0 0 0 RO 0 0 0.54 0 0.67 0 0 0 0 1.36 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.6163 0.5136 0.6018 0.6015 0.6631 0.6117 0.5538 0.6129 0.6509 0.6418 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0 0.0050 0 0.0276 0 0 0 0 0 0.0638 (ZnO + Li₂O) ZnO/ 0.3518 0.3057 0.3967 0.4166 0.4257 0.3778 0.4301 0.3853 0.4254 0.4567 (B₂O₃ + SiO₂) (ZrO₂ + Y₂O₃)/ 0.5934 0.5983 0.4071 0.3612 0.4196 0.487 0.4814 0.3965 0.4317 0.4144 (Nb₂O₅ + Gd₂O₃) nd 1.76958 1.77236 1.77415 4.77256 1.77422 1.77463 1.77458 1.77452 1.77406 1.77409 vd 49.57 48.26 48.37 49.62 49.89 49.52 49.57 49.50 49.51 49.67 ρ (g/cm³) 4.511 4.520 4.517 4.703 4.561 4.511 4.517 4.508 4.512 4.505 λ80/λ5 384/285 380/281 387/284 384/285 382/283 386/285 380/280 381/297 378/279 380/282 Tg (° C.) 614.2 615.1 620.3 617.5 616.2 614.3 614.7 615.0 611.8 615.2

TABLE 7 Embodiment Composition 61 62 63 64 65 66 67 68 69 70 SiO₂ 0.92 2.14 0.63 1.18 0.36 1.25 1.44 0.83 1.10 0.53 B₂O₃ 31.37 28.69 32.05 33.16 29.65 30.39 32.41 31.25 29.96 32.41 La₂O₃ 21.82 35.18 26.17 31.27 30.82 30.25 30.57 29.54 28.94 31.50 Gd₂O₃ 24.00 12.36 14.47 14.15 16.3 19.30 15.25 18.3 17.36 15.51 Y₂O₃ 1.12 0.88 0 1.33 3.09 0 0 2.15 0 0.65 Ta₂O₅ 0 0 0 0 0 0 0.18 0 0 0 Nb₂O₅ 0 0.16 0 0 0 0 0 0 0 0 ZrO₂ 7.36 6.59 7.09 6.68 7.15 6.94 7.54 6.78 7.22 6.88 ZnO 12.06 13.58 18.33 12.23 12.55 11.36 12.5 11.06 15.14 12.2 Bi₂O₃ 0 0 0 0 0 0 0 0 0 0 GeO₂ 0 0 0 0 0 0 0 0 0 0.32 Al₂O₃ 1.03 0 0 0 0 0 0 0 0.28 0 Li₂O 0 0.42 0.92 0 0.08 0.45 0 0.09 0 0 Na₂O 0 0 0 0 0 0 0.11 0 0 0 K₂O 0.32 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0 0.06 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 RO 0 0 0.28 0 0 0.06 0 0 0 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.4648 0.7266 0.6439 0.6689 0.6138 0.6105 0.6672 0.5909 0.6251 0.6609 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0 0.0114 0 0 0 0 0.0144 0 0 0 (ZnO + Li₂O) ZnO/ 0.3735 0.4405 0.5609 0.3561 0.4182 0.3590 0.3693 0.3448 0.4874 0.3704 (B₂O₃ + SiO₂) (ZrO₂ + Y₂O₃)/ 0.3533 0.5966 0.4900 0.5661 0.6282 0.3596 0.4944 0.4880 0.4159 0.4855 (Nb₂O₅ + Gd₂O₃) nd 1.77452 1.78203 1.77458 1.77406 1.79012 1.77415 1.77462 1.77451 1.77405 1.76214 vd 48.95 49.52 48.36 47.59 49.57 49.68 49.57 49.52 49.50 49.37 ρ (g/cm³) 4.517 4.633 4.534 4.571 4.516 4.503 4.511 4.520 4.784 4.515 λ80/λ5 385/284 381/281 382/280 385/284 382/281 382/280 380/282 381/280 381/282 380/280 Tg (° C.) 615.2 614.8 613.3 615.0 614.7 616.2 614.5 622.0 614.2 614.5

TABLE 8 Embodiment Composition 71 72 73 74 75 76 77 78 79 80 SiO₂ 1.26 0.92 0.75 1.35 1.18 0.78 0.59 0.69 0.84 0.37 B₂O₃ 30.33 31.25 30.41 32.39 32.85 31.05 29.64 31.04 32.33 31.2 La₂O₃ 29.34 29.15 30.3 28.44 29.14 27.94 31.36 29.66 30.94 29.04 Gd₂O₃ 16.72 16.32 17.29 16.95 15.67 16.22 19.27 18.32 18.47 17.55 Y₂O₃ 1.64 0 1.46 0 0 3.62 0 0.87 0 0 Ta₂O₅ 0 0.47 0 0 0 0 0 0 0 0.15 Nb₂O₅ 0.33 1.22 0 0 0.35 0 0 0 0 0.24 ZrO₂ 6.95 6.84 7.09 6.99 7.18 7.58 7.39 6.59 7.2 6.91 ZnO 13.07 13.55 12.11 11.82 13.06 12.17 11.25 12.67 10.22 13.94 Bi₂O₃ 0 0 0 0 0 0.64 0 0 0 0 GeO₂ 0 0 0.37 0 0 0 0 0 0 0 Al₂O₃ 0 0 0.08 0 0 0 0 0 0 0 Li₂O 0.36 0.28 0 0 0.57 0 0.35 0.16 0 0.34 Na₂O 0 0 0.14 0 0 0 0.15 0 0 0.26 K₂O 0 0 0 2.06 0 0 0 0 0 0 Sb₂O₃ 0 0 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 RO 0 0 0 0 0 0 0 0 0 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.6151 0.6411 0.6177 0.6266 0.6503 0.5848 0.6194 0.6072 0.6262 0.6233 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0.0246 0.1222 0 0 0.0257 0 0 0 0 0.0273 (ZnO + Li₂O) ZnO/ 0.4137 0.4212 0.3886 0.3503 0.3838 0.3823 0.3721 0.3993 0.3081 0.4416 (B₂O₃ + SiO₂) (ZrO₂ + Y₂O₃)/ 0.5038 0.3900 0.4945 0.4124 0.4482 0.6905 0.3835 0.4072 0.3898 0.3884 (Nb₂O₅ + Gd₂O₃) nd 1.77421 1.77430 1.77458 1.77405 1.77406 1.77400 1.77452 1.77415 1.77452 1.77506 vd 49.51 49.60 49.55 49.72 49.39 49.42 49.50 49.51 49.22 49.50 ρ (g/cm³) 4.510 4.506 4.517 4.528 4.533 4.517 4.500 4.487 4.523 4.516 λ80/λ5 381/280 383/282 382/282 382/281 380/281 381/279 380/282 380/284 381/280 380/280 Tg (° C.) 614.3 614.2 614.5 615.0 614.3 614.1 615.2 614.7 614.5 613.9

TABLE 9 Embodiment Composition 81 82 83 84 85 86 87 88 89 90 SiO₂ 0.34 0.85 0.69 1.08 0.59 0.73 0.84 0.45 0.28 0.71 B₂O₃ 33.19 31.06 29.33 30.84 34.19 35.17 32.06 31.52 30.17 32.25 La₂O₃ 28.15 31.48 31.08 29.32 26.24 25.21 29.55 30.36 29.66 30.94 Gd₂O₃ 16.43 16.19 14.9 15.67 18.23 18.15 17.59 17.00 16.47 13.33 Y₂O₃ 1.54 0 1.75 2.08 0 0.97 0 0 2.16 1.68 Ta₂O₅ 0 0.12 0.37 0 0 0 0 0 0 0 Nb₂O₅ 0 0 0.16 0 0 0.22 0 0 0 0 ZrO₂ 7.69 6.99 7.84 7.94 6.82 7.39 7.45 7.6 6.95 7.59 ZnO 12.30 12.06 13.25 13.07 13.47 12.04 12.6 13.07 12.26 13.50 Bi₂O₃ 0 0 0 0 0 0 0 0 0 0 GeO₂ 0 0 0 0 0.35 0 0 0 0 0 Al₂O₃ 0.36 0 0 0 0 0 0 0 0.04 0 Li₂O 0 0.16 0.63 0 0 0.12 0 0 0.95 0 Na₂O 0 0.32 0 0 0.11 0 0 0 0 0 K₂O 0 0 0 0 0 0 0 0 0 0 Sb₂O₃ 0 0.05 0 0 0 0 0 0 0 0 CeO₂ 0 0 0 0 0 0 0 0 0 0 RO 0 0.72 0 0 0 0 0 0 1.06 0 Total 100 100 100 100 100 100 100 100 100 100 La₂O₃/(La₂O₃ + 0.6104 0.6604 0.6512 0.6229 0.5901 0.5687 0.6269 0.6410 0.6142 0.6733 Gd₂O₃ + Y₂O₃) (Ta₂O₅ + Nb₂O₅)/ 0 0.0098 0.0382 0 0 0.0181 0 0 0 0 (ZnO + Li₂O) ZnO/ 0.3668 0.3779 0.4414 0.4095 0.3873 0.3354 0.3830 0.4088 0.4026 0.4096 (B₂O₃ + SiO₂) (ZrO₂ + Y₂O₃)/ 0.5618 0.4317 0.6368 0.6394 0.3741 0.4551 0.4235 0.4471 0.5531 0.6954 (Nb₂O₅ + Gd₂O₃) nd 1.76592 1.77504 1.77462 1.77406 1.78226 1.77515 1.77463 1.77485 1.77406 1.77428 vd 49.57 49.68 49.58 49.63 49.39 49.77 49.58 49.50 49.75 49.62 ρ (g/cm³) 4.506 4.517 4.603 4.557 4.532 4.526 4.521 4.503 4.518 4.509 λ80/λ5 382/281 380/281 382/282 380/281 380/280 381/283 380/280 382/281 379/280 380/280 Tg (° C.) 615.7 616.0 614.3 614.2 615.3 617.2 614.2 614.0 614.1 613.8

[Optical Preform Embodiment]

The optical glass obtained from Embodiment 1 in Table 1 is cut into the predetermined size, and the releasing agent is uniformly coated on the surface. Then, the glass is heated, softened and press-molded to produce the preforms of various lenses and prisms, including concave meniscus lens, convex meniscus lens, biconvex lens, biconcave lens, planoconvex lens and planoconcave lens.

[Optical Element Embodiment]

The preforms obtained in the above-mentioned optical preform embodiment are annealed for fine-tuning while the deformation inside the glass is reduced, so that the optical characteristics such as the refractive index are brought to the desired values.

Then, each preform is ground and polished to form a variety of lenses and prisms such as concave meniscus lens, convex meniscus lens, biconvex lens, biconcave lens, planoconvex lens and planoconcave lens. An anti-reflection film may be coated on the surface of the obtained optical element.

The present invention provides a high-refraction low-dispersion optical glass having a low cost and excellent transmittance, with refractive index of 1.76-1.80 and Abbe number of 47-51, and an optical element made of the glass, which can meet the demands of modern novel photoelectric products. 

1. An optical glass, comprising the following components by weight percentage: 0-3% of SiO₂; 25-40% of B₂O₃; 20-40% of La₂O₃; 12-25% of Gd₂O₃; 6.5-15% of ZrO₂; greater than 10% but less than or equal to 20% of ZnO; 0-5% of Ta₂O₅; 0-5% of Nb₂O₅; 0-10% of Li₂O; less than 0.45 of (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O); 0-10% of Y₂O₃.
 2. The optical glass according to claim 1, further comprising 0-10% of GeO₂; 0-10% of Bi₂O₃; 0-10% of Al₂O₃; 0-10% of Na₂O; 0-10% of K₂O; 0-1% of CeO₂; 0-1% of Sb₂O₃; 0-10% of RO, in which RO is one or more of MgO, CaO, SrO or BaO.
 3. The optical glass according to claim 2, comprising 0-5% of Al₂O₃ and/or 0-5% of Na₂O and/or 0-5% of K₂O and/or 0-5% of GeO₂ and/or 0-5% of Bi₂O₃ and/or 0-0.5% of CeO₂ and/or 0-0.5% of Sb₂O₃ and/or 0-5% of RO.
 4. The optical glass according to claim 2, comprising 0-1% of Al₂O₃ and/or 0-1% of Na₂O and/or 0-1% of K₂O and/or 0-1% of GeO₂ and/or 0-1% of Bi₂O₃ and/or 0-1% of RO.
 5. The optical glass according to claim 1, wherein (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is 0.30-1.50; La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.38-0.75; ZnO/(B₂O₃+SiO₂) is 0.25-0.65.
 6. The optical glass according to claim 1, comprising 28.5-35% of B₂O₃ and/or 25-35% of La₂O₃ and/or 14-22% of Gd₂O₃ and/or 6.5-10% of ZrO₂ and/or 11-16% of ZnO and/or 0-1% of SiO₂ and/or 0-1% of Ta₂O₅ and/or 0-1% of Nb₂O₅ and/or 0-7% of Y₂O₃ and/or 0-5% of Li₂O.
 7. The optical glass according to claim 1, comprising 29-32% of B₂O₃ and/or 27-32% of La₂O₃ and/or 15-20% of Gd₂O₃ and/or 6.5-8.5% of ZrO₂ and/or 11-14.5% of ZnO and/or 0-0.5% of SiO₂ and/or 0-0.5% of Ta₂O₅ and/or 0-0.5% of Nb₂O₅ and/or 0.1-5% of Y₂O₃ and/or 0-1% of Li₂O.
 8. The optical glass according to claim 1, wherein (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) is less than 0.10; and/or La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.45-0.70; and/or ZnO/(B₂O₃+SiO₂) is 0.30-0.55; and/or (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is 0.48-1.10.
 9. The optical glass according to claim 1, wherein (Ta₂O₅+Nb₂O₅)/(ZnO+Li₂O) is less than 0.07; and/or La₂O₃/(La₂O₃+Gd₂O₃+Y₂O₃) is 0.55-0.65; and/or ZnO/(B₂O₃+SiO₂) is 0.30-0.50; and/or (ZrO₂+Y₂O₃)/(Nb₂O₅+Gd₂O₃) is 0.50-1.0.
 10. The optical glass according to claim 1, wherein the glass refractive index is 1.76-1.80; the Abbe number is 47-51; the density is below 5.00g/cm³; and the transition temperature Tg is below 625° C.
 11. A glass preform, made of the optical glass according to claim
 1. 12. An optical element, made of the optical glass according to claim
 1. 